Glo-Protect PU Aliphatic Coat 1673

High-build, Two-component, High-Solids Acrylic Polyurathne Coat

Glo-Protek PU Aliphatic Coat 1673 is a high-build, two-component, high-solids acrylic polyurathne coating and it offers excellent resistance to atmospheric exposure conditions. It offers very good resistance to water and saline atmosphere. It also offers resistance to splash and spillage of mild chemicals and gives tough and abrasion resistant finish on curing


Colour Range
Finish Satin-Eggshell
Volume Solids Approx. 64%
Recommended DFT/COAT 50 - 125 microns
Mixing Ratio 8 : 1 by volume
Pot Life 2 - 3 hours (30ºC)
Theoretical spreading rate 12.80 - 5.10 m /l at above DFT
Touch Dry 1 - 1.5 hours at 30ºC
Hard Dry 16 hours
Fully cured 7 days at 30ºC
Overcoating Interval Min: 16 hours; Max: 7 days
Flash point Above 27ºC
Thinner PU thinner

Surface Preparation

The substrate surface/previous coat should be dry and free from all surface contaminations. The indicated maximum recoating interval refers to over-coating with itself. However, if applied over old painted surface, then the substrate surface should be roughened sufficiently before applying the coat.

Method of Application

By Air Spray, Airless Spray, Brush
A two-coat application is recommended to achieve optimum results when applied by brush.

Standard Packing

18-litre drums


Store in sealed containers under cool and dry conditions.
Store in accordance with local regulations.

Health & Safety

As a general safety precaution, care should be taken to avoid contact of liquid paint with skin and eyes, and i confined spaces nhalation of solvent vapors or paint mist should be avoided. Air movement should be ensured with proper forced ventilation when applying the paint in . Skin, eye and respiratory protection is always recommended at all times while coating.