Glo-Protect PU Aliphatic Coat 1637
Two-component, Acrylic Aliphatic Polyurethane Coat
Glo-Protek PU Aliphatic Coat 1637 is a two-component, acrylic aliphatic polyurethane coating having an excellent gloss and color retention. It has excellent resistance to water, chemicals, impact, abrasion and industrial corrosive atmosphere.
It is used for a variety of substrates such as steel, aluminum, glass-fiber reinforced polyester, plywood, where light fastness and gloss retention is desired as an excellent finish coat.
TECHNICAL DATA
Colour | Range |
---|---|
Finish | High glossy |
Volume Solids | Approx. 45% |
Recommended DFT/COAT | 25 - 35 microns |
Mixing Ratio | 4 : 1 by volume |
Pot Life | 4 - 5 hours (30ºC) |
Nozzle Orifies | 0.017 - 0.019 inch |
Theoretical spreading rate | 18.00 - 12.85 m /l at above DFT |
Surface Dry | 1 hours at 30ºC |
Hard Dry | 16 hours |
Fully cured | 7 days at 30ºC |
Overcoating Interval | Min: 16 hours; Max: 7 days |
Flash point | 27ºC |
Thinner | PU thinner |
Surface Preparation
The substrate surface/previous coat should be dry and free from all surface contaminations. The indicated maximum re-coating interval refers to over-coating with itself. Suitable Epoxy Primer/ Inter coat surfaces should be dry and free from dirt, dust etc before top-coating with Glo-Protek PU COAT 1674. However, if applied over old painted surface, then the substrate surface should be roughened sufficiently before applying the coat.
Method of Application
By Air Spray, Airless Spray, Brush
Standard Packing
20-litre drums
Storage:
Store in a cool, dry place
Health & Safety
As a general safety precaution, care should be taken to avoid contact of liquid paint with skin and eyes, and i confined spaces nhalation of solvent vapours or paint mist should be avoided. Air movement should be ensured with proper forced ventilation when applying the paint in . Skin, eye and respiratory protection is always recommended at all times while coating.